Product Description
Product features
1. HDPE geomembrane is a flexible waterproof material with a high permeability coefficient (1× 10-17cm /s).
2. HDPE geomembrane has good heat and cold resistance. Its operating environment temperature is 110℃ at high temperature and -70℃
at low temperature.
3, HDPE geomembrane have good chemical stability, can resist strong acid, alkali, oil corrosion is a good anticorrosive material.
4. HDPE geomembrane has high tensile strength, which enables it to meet the requirements of high-standard engineering projects.
5. HDPE geomembrane have strong weather resistance and anti-aging performance, which can be used naked for a long time while
maintaining the original performance.
6, the overall performance of HDPE geomembrane, HDPE geomembrane has a strong tensile strength and fracture elongation, so that
HDPE geomembrane can be used in a variety of harsh geological and climatic conditions.Strong adaptability to geological
non-uniform subsidence stress.
7.HDPE geomembrane are made of high quality primary plastics and carbon black particles without any preservatives
Specification
HDPE Geomembrane Technical Parameter |
Properties | Test Method | Test thickness |
0.75mm | 1.00 mm | 1.50 mm | 2.00 mm | 2.50mm | 3.00mm |
Thickness - mils (min. ave.)·
lowest individual of 10 values | D5199 | nom. (mil)
-10% | nom. (mil)
-10% | nom. (mil)
-10% | nom. (mil)
-10% | nom. (mil)
-10% | nom. (mil)
-10% |
Density (min.) | D 1505/
D 792 | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc |
Tensile Properties (1) (min. ave.)·
yield strength·
break strength·
yield elongation·
break elongation | D 6693
Type IV | 11 kN/m
20 kN/m
12%
700% | 15 kN/m
27 kN/m
12%
700% | 22 kN/m
40 kN/m
12%
700% | 29 kN/m
53 kN/m
12%
700% | 37 kN/m
67 kN/m
12%
700% | 44 kN/m
80 kN/m
12%
700% |
Tear Resistance (min. ave.) | D 1004 | 93N | 125 N | 187 N | 249 N | 311 N | 374 N |
Puncture Resistance (min. ave.) | D 4833 | 240N | 320 N | 480 N | 640 N | 800 N | 960 N |
Stress Crack Resistance (2) | D 5397(App.) | 300 hr. | 300 hr. | 300 hr. | 300 hr. | 300 hr. | 300 hr. |
Carbon Black Content - % | D 4218 (3) | 2.0-3.0% | 2.0-3.0% | 2.0-3.0% | 2.0-3.0% | 2.0-3.0% | 2.0-3.0% |
Carbon Black Dispersion | D 5596 | note (4) | note (4) | note (4) | note (4) | note (4) | note (4) |
Oxidative Induction Time (OIT)
(min. ave.) (5)
(a) Standard OIT— or —
(b) High Pressure OIT | D 3895
D 5885 | 100 min.
400 min. | 100 min.
400 min. | 100 min.
400 min. | 100 min.
400 min. | 100 min.
400 min. | 100 min.
400 min. |
Oven Aging at 85°C (5), (6)
(a) Standard OIT (min. ave.)
- % retained after 90 days— or —
(b) High Pressure OIT (min. ave.)
- % retained after 90 days | D 5721
D 3895
D 5885 | 55%
80% | 55%
80% | 55%
80% | 55%
80% | 55%
80% | 55%
80% |
UV Resistance (7)
(a) Standard OIT (min. ave.)— or —
(b) High Pressure OIT (min. ave.)
- % retained after 1600 hrs | D 3895
D 5885 | N.R. (8)
50% | N.R. (8)
50% | N.R. (8)
50% | N. R. (8)
50% | N. R. (8)
50% | N. R. (8)
50% |